Basic product description

Polyester conveyor belts (EP conveyor belts) are widely used in coal, mining, ports, metallurgy, electric power, chemical industry and other fields to transport materials

Features：

High strength, high belt body and light weight
2. Use EP dipped canvas as skeleton material
3. The belt body is soft, has good troughing properties and good elasticity
4. Impact resistance, wear resistance and corrosion resistance
5. Adapt to larger load capacity, faster speed and medium and long distance material transportation
6. Smooth operation and no deviation

Polyester multi-layer conveyor belt specifications and technical parameters

Fabric Type	Fabric Construction		Fabric model	Tape thickness	Strength series (N/mm)
Fabric Type	through	latitude	Fabric model	Tape thickness	2 layer	3 layer	4 layer
Polyester (EP)	Polyester	Nylon	EP-100	1.00	200	300	400
			EP-125	1.05	250	375	500
			EP-150	1.10	300	450	600
			EP-170	1.10	340	510	680
			EP-200	1.20	400	600	800
			EP-250	1.40	500	750	1000
			EP-300	1.60	600	900	1200
			EP-350	1.70		1050	1600

Adhesion strength and extension performance are in accordance with the table below

Core material	Adhesion strength
	Between fabric layers (N/mm)	Between covering layer and cloth layer (N/mm)
		Covering layer thickness ≤1.5mm	Covering layer thickness ≥1.5mm
polyester canvas	≥5	≥4.5	≥5
Extended performance
Full thickness longitudinal tensile elongation at break		Full thickness longitudinal reference force elongation
≥10%		≤4%

The covering performance of the tape complies with the following table

Coverage level	Tensile Strength	Elongation at break	Amount of wear	Change rate of tensile strength and elongation at break after aging
Coverage level	Mpa	%	mm³	%
H	24	450	120	-25~+25
D	18	400	100	-25~+25
L	15	350	200	-25~+25